A New Approach for Modelling Glass Fracture

Event Description

The simulation of safety glass, used for windshield applications in the automotive industry, is still a challenging topic for commercial crash solvers. Holistic modelling of the behaviour of glass has become more important due to its influence on structural behaviour in several load cases, such as dynamic crashworthiness and pedestrian protection.

The main requirement from the industry is to use the same model and the same mesh for all load cases. The commonly used element erosion technique for the representation of failure in explicit analyses leads to a significant underestimation of the stress at the crack tip and thus of the crack pattern in the simulation. Local refinement, such as adaptive meshing, will lead to localization, and ultimately to failure in the refined area. Local refinement can be a suitable method for stamping simulation where the final deformed shape is known, but it is not recommended in crash applications. To overcome drawbacks with local refinement, Altair previously implemented the eXtended Finite Element Method ‘X-FEM’ in the crash solver Altair Radioss. There is still ongoing research and development on improving the quality of the results of the prediction of the stiffness and fracture of glass as used in windshield applications.

In addition to the X-FEM approach, a non-local failure method was developed by Christian Alter et al. This failure model uses a decrease of the rate dependent fracture stress in the direction of a propagating crack instead of an upscaling of the stress tensor. The Model was validated in the context of head impact on windshields and is already available in Altair Radioss (as the /FAIL/ALTER failure model). The Christian Alter failure model was further enhanced by a feature developed by Christopher Brokmann to account for the existence of initial micro-cracks in the glass structure. This research and development was done within a public funded research project, using a stochastic approach to model this physical phenomenon. It is also embedded into the most recent implementation of the Radioss /FAIL/ALTER failure criterion. These enhancements allow the consideration of the stochastic behaviour of crack initiation as well as accounting for the thermally or chemically treated outer surface of a single layer glass.

These new features extend the range of applications for glass failure modelling from automotive windshields to consumer goods where tempered glass is used. For example: within the consumer electronics industry for smartphone screens.

About this event

This event is being hosted by the NAFEMS Impact, Shock and Crash Working Group. For more information and to get involved go to the Impact, Shock and Crash Working Group webpage.

The ISCWG has formed an online Community to enable NAFEMS members to learn more and interact with other engineers and scientists who have an interest in Impact, Shock and Crash analysis. For more information and to get involved go to the ISC Community webpage.

Document Details

AuthorsSharp. P Bulla. M
TypePresentation Recording
Date 20th September 2022
OrganisationAltair Engineering


Back to Previous Page